posted on July 23rd, 2013 at 02:05 PM
Leading, Body solder, body wipe


Does anyone know of somwhere near Brisbane that can do this?
Alt who does good panel work. lots of small holes etc in bottom of front and rear gaurds. (usual spots)
Also some larger ones which would require a bit more work.
Was going to have a crack at this but is getting a it daughting and time is hard to find at the mo.
Really want to try and stay away from the putty quick fix if possible.
Also the bottom of one of the doors has a large hole in the bottom of the door, only visable from bottom,is on the inside and not visable from out side.
Is this repairable or a waste of time. would like to try and keep all as i got.
Left hard drive at home with pic's will post some later.
MemberHappyDaze
A.k.a.: Greg Mackie
Son of Jim - Creator of Good
Superannuated
******


Avatar


Posts: 2887
Threads: 141
Registered: June 13th, 2009
Member Is Offline

Location: Southern Highlands NSW
Theme: UltimaBB Pro Blue ( Default )
Mood: Happy enough

posted on July 23rd, 2013 at 02:42 PM



Sound like a bit more than lead-wiping required, although it's hard to tell without seeing the damage.

I did quite a bit of lead-wiping in the '50s - early '60s, but lead is not good over rust. Pity you are so far away, or I could give some lead-wiping lessons.




I'd rather wear a Beetle out by racing it than by polishing it!
Super Administratorvw54
Super Administrator
Always Waiting 4 Friday
*********

Rank Avatar

No Avatar


Posts: 16723
Threads: 378
Registered: August 26th, 2002
Member Is Offline

Location: Sunny Sydney
Theme: UltimaBB Pro Blue ( Default )
Mood: Oval resto ongoing

posted on July 23rd, 2013 at 07:47 PM



yep Lead wiping is really only for the seams in the old days before BOG was invented

hardtop do as you must have a ultra clean surface and require a good flux also

nothing wrong with the plastic body filler these days much easier to use and safer ( also you must have a good clean surface to bond to )




Super Administratorhelbus
A.k.a.: Pete S
Super Administrator
Mad fabricator, paint and body
*********

Rank Avatar

Avatar


Posts: 7386
Threads: 312
Registered: September 1st, 2002
Member Is Offline

Location: In the garage chopping cars into bits
Theme: UltimaBB Pro Blue
Mood: In the thinking chair

posted on July 23rd, 2013 at 08:04 PM



I only ever use lead for seams, joins and edges. Lead is not to 'cover' rust holes. Unfortunatley once you have holes on the outside you will have much more you cant see still. The proper way is to cut out all of the affected area and replace it.



MemberMatty v
Commited Dubber
**


No Avatar


Posts: 55
Threads: 13
Registered: July 29th, 2010
Member Is Offline

Theme: UltimaBB Pro Blue ( Default )

posted on July 24th, 2013 at 08:17 AM



Thanks for the replies, i have been cutting and welding in patches, (fun weliding such thin material) for the larger holes etc, the areas i was thinking about leading are areas where there is pitting not all the way through the panel, sort of on the curve/bends. appears to have cleaned up quite well but may just have to look at the plastic stuff.
Will post some piccies when i get a chance for your opinion.
Shame im not closer happdayz for sure, i would still love to check out this old practice and try and keep the skill alive.
Thanks for the advice, trying to sort this has slowed my restro but in no rush.
Membervlad01
Compulsive Aussie Vee Dubber
*******


Avatar


Posts: 4270
Threads: 109
Registered: June 3rd, 2010
Member Is Offline

Location: Kyneton, VIC
Theme: UltimaBB Pro Blue ( Default )
Mood: Side ways

posted on July 25th, 2013 at 11:46 AM



Quote:
Originally posted by Matty v
Thanks for the replies, i have been cutting and welding in patches, (fun weliding such thin material) for the larger holes etc, the areas i was thinking about leading are areas where there is pitting not all the way through the panel, sort of on the curve/bends. appears to have cleaned up quite well but may just have to look at the plastic stuff.
Will post some piccies when i get a chance for your opinion.
Shame im not closer happdayz for sure, i would still love to check out this old practice and try and keep the skill alive.
Thanks for the advice, trying to sort this has slowed my restro but in no rush.


you will have real difficultly lead filling pitted areas, been there done that. even sand blasted clean the flux and lead was hard to flow.


As hellbus said, need to be perfect and super clean metal for it to be effective.

Its good on joins and overlaps, seams and minor dents that can't re otherwise accessed via panel beating tools.

beats the hell out of bog imho, wont touch that shit!




http://i1015.photobucket.com/albums/af278/vladk01/notch04.png